Preparação e propriedades de crásticos refratários de baixo cimento
Tecnologia de preparação e propriedades básicas
Baixo cimento Castabas refratáriasare carefully designed and screened, and the samples are made under the best process conditions and cured under natural conditions. Its 3d room temperature compressive strength reaches 15.45MPa, and its performance is more stable after drying. This castable is based on aluminum silicate, uses first-grade clay clinker and first-grade to special-grade alumina clinker as aggregates, and is combined with refractory powders such as special-grade or first-grade alumina clinker powder and brown corundum powder, as well as ultrafine powders such as -Al2O3 powder and silica fume, and adds an appropriate amount of composite water reducer. With the increase of heating temperature, the strength of the castable increases significantly, and the strength at 1500℃is about 1 times higher than that when seco . Sua resistência e estabilidade de flexurais de alta temperatura também são melhores que CA -50 Cement Castables refratários . Além disso, a temperatura de refratório de baixo cimento é tão alta quanto a temperatura de refratões (a temperatura de amadurecimento de carga »» »de 20 de grau de cimento… também aumentou de acordo.
Desempenho de alta temperatura e características de expansão térmica
During the heating process, the thermal expansion rate of the castable increases first and then decreases, reaching a maximum value of 0.68% at 1250℃, and then begins to shrink slowly, but the thermal expansion rate rises slightly at 1500℃. The high strength of this high-performance castable and the increase in medium-temperature strength are due to the fact that the O processo de desidratação do hidrato de aluminato de cálcio é lento e contínuo em uma grande faixa de temperatura e tem pouco dano à estrutura cristalina . Esta convergência de expansão térmica bem controlada permite que os cráticas refratários de baixo cimento exibam melhor resistência e estabilidade em alta temperatura.
Estrutura dos poros e análise de porosidade
The molded body of the refractory castable presents a heterogeneous structure with a small amount of pores, in which the size and number of pores have a direct impact on the performance of the castable. By mercury intrusion, we determined the pore size distribution of the two castables. The results show that the pore size of the low-cement refractory castable is mainly distributed in the range of no more than 100nm, representando 70 . 7% a 73 . 2%, que é 2 a 3 vezes maior que o do CA -50 Cement Refratário Castável . após a seca em 110 graus, a porosidade total dos dois castelos é equivalente a {17} { the low-cement refractory castable only increased by about 6%, while that of the CA-50 cement castable increased by nearly 39%. This result reveals that the low-cement refractory castable has the characteristics of small total pore volume, many small capillaries and uniform distribution, that is, low porosity, excellent pore structure, poor permeability and strong resistance to slag erosion. Após o tratamento do aquecimento, mostra a vantagem da distribuição de tamanho de poro pequeno e aumenta a resistência a danos.
Resistência a escória e aplicação de castáveis refratários de baixo cimento
Comparação de resistência à escória e resultados dos testes
Low-cement refractory castables show significant advantages in slag erosion resistance. Through the rotary method test, we found that when the low-cement castable is heated to 1400℃and maintained at a rotation speed of 6r/min in a blast furnace slag medium, its slag erosion depth is only 1.25mm, which is much better than the 2 . 65 mm do castável ligado a argila . ao mesmo tempo, também descobrimos que quanto menos cimento é usado, melhor a resistência à erosão da escória; Quanto maior o grau de cimento, mais forte a resistência à erosão da escória do cimento de baixo cimento formulado . especificamente, o castável formulado com Ca -70 cimento é melhor que a resistência à erosão, e a quantidade de erosão é reduzida por uma quantidade de resistência à erosão. Os castáveis de baixo cimento mostram uma melhor resistência à erosão da escória do que o CA -50 cimento, de cimento, especialmente sob as condições de escória do forno de alta temperatura, a profundidade da penetração é pequena.
Aplicação em equipamentos térmicos
Os castéis de baixo cimento de baixo cimento são amplamente utilizados em vários equipamentos térmicos devido à suas boas características de resistência e resistência ao fogo ., elas não apenas têm um bom desempenho em fornos industriais em geral, mas também são particularmente adequados para altas temperaturas e ambientes de rescrito em rescrato de desgaste (2}}, por exemplo, retenções de relevo e rescrato de rescrato em relevo em relevo em relevo em reletos e refratários em reletos em reletos e retenções de retenção de relevo em relevo, refratários de rescrito em reletos e rescrativos em reletos e retenções de retenção de retenção de retenção de relevo em relevo, retenções de relevo em relevo, retenções de retenção de relevo em relevo e rescrfeto de rescrativo equipment. Among them, mullite and corundum castables play an important role in the lining of steel rolling heating furnaces, water cooling pipe wrapping and burner bricks with their excellent performance. SiC refractory castables, with their low linear expansion coefficient, high thermal conductivity, high strength and wear resistance, perform well in thermal equipment such as power generation boilers, non-ferrous Fornos e incineradores metalúrgicos . O castável não apenas tem uma boa resistência ao choque térmico, mas também tem a vantagem da condutividade térmica, que é um pouco mais alta do que outros castáveis devido à baixa porosidade e estrutura densa .